ARMOPUR® TOPCOAT 264 Semi‑gloss
Two‑component semi‑gloss acrylic‑polyurethane enamel. An aliphatic isocyanate is used as the curing agent. Also used as a 2K basecoat for subsequent overcoating with acrylic lacquers. Applied to large surfaces such as passenger trains, buses, trolleybuses, trams, truck cabins.
Specific Feature
metallic effect
Product Chemistry
acrylic‑polyurethane
Color Options
colored according to ral, ncs and sample
Surface Type
2K primers
Gloss Level
semi‑gloss
- Applied to a primed surface;
- Features accelerated polymerization;
- Forms an atmospheric‑resistant coating capable of retaining color and gloss over a prolonged service life;
- Suitable for use as a semi‑gloss topcoat in systems with epoxy and acrylic‑polyurethane primers;
- For enhanced protective‑decorative performance, it is recommended to additionally coat with a 2K acrylic‑polyurethane varnish;
- Recommended for painting transport, equipment, exterior surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Solid content of the mixture: 44 ± 2%.
- Solid content of the base: 50–60%.
- Mixture density: 1.1–1.3 kg/L.
- Base viscosity: >180 s (DIN 4).
- Mixture viscosity: 40–70 s (DIN 4).
- Mixture pot life: 3 h.
- Drying time for a dry film thickness of 50 µm:
- +10 °C:
- "Dust resistance": 30 min
- "Touch‑off": 3 h
- Minimum intercoat drying: 15 min
- +23 °C:
- "Dust resistance": 20 min
- "Touch‑off": 2 h
- Minimum intercoat drying: 5–7 min
- +35 °C:
- "Dust resistance": 10 min
- "Touch‑off": 1 h
- Minimum intercoat drying: 5 min
- Thermal drying:
- +60 °C: 30 min
Complete coating formation: 7 days under natural drying.
Data are given at 65 % relative humidity. Values may change with humidity variations.