ARMOPUR® DTM 113 SEMIGLOSS
Primer‑finish coating two‑component semi‑gloss acrylic‑polyurethane anticorrosive, weather‑resistant. An aliphatic polyisocyanate is used as the hardener.
Gloss - 36‑60% depending on the color;
Specific Feature
thick‑coat application
Product Chemistry
acrylic‑polyurethane
Color Options
Colored according to RAL, NCS and sample
Surface Type
steel
galvanized steel
aluminum
plastics (except PP and PE)
2K primers
Gloss Level
semi‑gloss
- When applied in two layers, it can be used as a standalone coating;
- Zinc phosphate is used as the anticorrosive pigment;
- Excellent resistance to atmospheric exposure and wear;
- Suitable for use as a semi‑gloss topcoat for epoxy and acrylic‑polyurethane systems exposed to atmospheric and/or chemical conditions;
- Recommended for painting transport vehicles, equipment, external surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Solid content of the mixture: 51 ± 2 % | *54 ± 2 %.
- Solid content of the base: 55–75 %.
- Mixture density: 1.1–1.2 kg/L.
- Base viscosity: >180 s (DIN4).
- Mixture viscosity: 65–85 s (DIN4).
- Mixture pot life: 4 h.
- Drying time for a 50 µm dry film thickness:
- +10 °C:
- Dry to dust: 30 min
- Recoat: 6 h
- Minimum intercoat drying: 15 min
- +23 °C:
- Dry to dust: 20 min
- Recoat: 4 h
- Minimum intercoat drying: 5–7 min
- +35 °C:
- Dry to dust: 10 min
- Recoat: 2 h
- Minimum intercoat drying: 5 min
- Temperature drying:
- +60 °C: 30 min
Complete film formation: 7 days under ambient drying.
Data are given at 65 % relative humidity. Values may change with humidity variation.
* Version with ARMOPUR Hardener 61 | 63