ARMOPUR® DTM 162 Gloss
Two‑component acrylic‑polyurethane glossy primer‑finish coating (gloss 70–80 %), developed as a Direct-to-Metal (DTM) solution. The coating provides excellent anticorrosion and weather‑resistant protection, allowing it to be applied directly to metal. An aliphatic isocyanate is used as the hardener, guaranteeing a durable and aesthetically attractive finish.
Specific Feature
thick‑coat application
Product Chemistry
acrylic‑polyurethane
Color Options
colored according to ral, ncs and sample
Surface Type
steel
aluminum
galvanized steel
plastics (except PP and PE)
2K primers
Gloss Level
glossy
- When applied in a two‑coat system, it can be used as a standalone coating;
- Zinc phosphate is used as the anticorrosion pigment;
- Excellent resistance to atmospheric exposure and wear;
- Suitable for use as a glossy topcoat on epoxy and acrylic‑polyurethane systems exposed to atmospheric and/or chemical attack;
- Recommended for painting vehicles, equipment, external surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Shows good adhesion to various plastics (except PE/PP);
- Forms a coating with enhanced chemical resistance.
- Solid content volume: 58 ± 2%.
- Solid content weight: 60–80%.
- Mixture density: 1.15–1.25 kg/L.
- Base viscosity: >180 s (DIN4).
- Mixture viscosity: thixotropic.
- Mixture pot life: 2 h.
- Drying time for a dry film thickness of 50 µm:
- +10 °C:
- Dust resistance: 30 min
- Tack‑free: 6 h
- Minimum intercoat drying: 15 min
- +23 °C:
- Dust resistance: 20 min
- Tack‑free: 5 h
- Minimum intercoat drying: 5–7 min
- +35 °C:
- Dust resistance: 10 min
- Tack‑free: 2 h
- Minimum intercoat drying: 5 min
- Thermal drying:
- +60 °C: 30 min
Full film formation: 5 days under ambient drying.
Data are given at 65 % relative humidity. Values may change with humidity variations.